S355J2W

2023-05-15 08:48:00 來源：鋼鐵之家閱讀量：0

牌號	S355J2W
歐標鋼號	1.8965
對應(yīng)標準	EN 10025-5-2019 熱軋結(jié)構(gòu)鋼-第5部分：耐候結(jié)構(gòu)鋼 Hot rolled products of structural steels-Part 5: Technical delivery conditions for structural steels with improved atmospheric corrosion resistance
歸類	合金鋼
標簽	耐候結(jié)構(gòu)鋼鎮(zhèn)靜鋼

S355J2W 化學元素成分含量(%)

	成分	C	Si	Mn	P	S	Cr	Ni ^③	Cu	Mo ^③	Zr ^③
長形產(chǎn)品	最小值	-	-	0.5	-	-	0.4	-	0.25	-	-
長形產(chǎn)品	最大值	0.16	0.5	1.5	0.03	0.03	0.8	0.65	0.55	0.3	0.15

	成分	C	Si	Mn	P	S	Cr	Ni ^③	Cu	Mo ^③	Zr ^③
	最小值	-	-	0.5	-	-	0.4	-	0.25	-	-
	最大值	0.16	0.5	1.5	0.035	0.035	0.8	0.65	0.55	0.3	0.15

①FN=rimming steels not permitted(不允許沸騰鋼)；FF=fully killed steel(完全鎮(zhèn)靜鋼)
②The steels contain at least one of the following elements: Al total≥0.02%，Nb:0.015~0.06%，V:0.02~0.12%，Ti:0.02~0.1%。If these elements are used in combination, at least one them shall be present with the minimum content indicated。(鋼應(yīng)至少含有下列元素之一:Al總含量為≥0.020%，Nb:0.015 ~ 0.060%，V:0.02 ~ 0.12%，Ti:0.02 ~ 0.10%。如果將這些元素組合使用，其中至少有一種元素應(yīng)具有所示的最低含量。)
③鋼中Ni、Mo、Zr含量可達的最大值
④當Si的最低含量為0.15%時，Cr含量可降至0.37%

碳當量計算

S355J2W 機械性能

厚度 t mm	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷后伸長率或延伸率 δ %
t＜3	510~680	≥355	見備注
3≤t≤16	470~630	≥355	≥22
16＜t≤40	470~630	≥345	≥22
40＜t≤63	470~630	≥335	≥21
63＜t≤80	470~630	≥325	≥20
80＜t≤100	470~630	≥315	≥20
100＜t≤150	450~600	≥295	≥18

①公稱厚度1.5＜t≤2時，斷后延伸率δ≥16
②公稱厚度2＜t≤2.5時，斷后延伸率δ≥17
③公稱厚度2.5＜t＜3時，斷后延伸率δ≥18

近似對照表結(jié)構(gòu)、壓力容器和工程鋼

日本	美國	德國	歐標
JIS	ASTM	DIN EN/DIN	EN	數(shù)字牌號
SMA50CP	A709-50W	WTSt52-3	S355J2W S355J2G2W①	1.8965

注：本資料來源于互聯(lián)網(wǎng)的公開資源整理，我們不保證這些資料的準確性、完整性和適用性。這些資料僅供您參考，不應(yīng)用于任何商業(yè)用途或決策依據(jù)。本資料所記載的技術(shù)信息是說明產(chǎn)品的代表性特點和性能的參考值，對于因誤用或不當使用本資料所記載的信息等而造成的損害恕難承擔責任，敬請周知。

上一篇：L485Q-PSL2
下一篇：30MnB5